Removing Cured Epoxy

Introduction
Epoxies have a wide range of applications in microscopy sample preparation and vacuum chamber feedthroughs or leak repairs. One of the advantages of cured epoxy is that it provides a permanent and strong bond in embedding and adhesive applications. However, the strong bond acts a restriction when it is needed to remove a sample from a cured epoxy embedding or when a sample or part needs to be de-bonded.

Solutions for Removing Cured Epoxies
Techniques for removing spilled epoxy, a sample from an epoxy embedding or an epoxy bond are given below. Please be aware that some of the techniques listed are destructive and can ruin the part or sample. Use safe working practices when removing epoxy. One should always check if the sample is compatible with the technique used. To remove cured epoxies use:

  1. Solvents
  2. Sulfuric acid
  3. Thermal decomposition
  4. Thermal shock
  5. Combination of heat and pressure
  6. Boiling water
  1. Solvents
  2. Chlorinated solvent aggressively attacks cured epoxy. Methylene chloride (dichloromethane) has been used successfully after soaking the material for several hours. Methylene chloride is one of the main components of commercially available epoxy removers. Other solvents which have shown to be effective are: toluene, MEK (methyl-ethyl-ketone) and NMP (n-methyl-pyrollidone)

  3. Sulfuric Acid
  4. A warm solution of sulfuric acid dissolves cured epoxy after soaking. For small amounts of epoxy, repeatedly dropping sulfuric acid on the epoxy is a useful technique and doesn’t require soaking.

  5. Thermal Decomposition
  6. Most epoxies will decompose and turn to carbon ash at temperatures above the degradation temperature. The degradation temperature should be listed on the data sheet of the epoxy. It is likely to be 400°C and higher

  7. Thermal Shock
  8. When substrate, epoxy and parts have large differences in thermal expansion rates, large temperature differences would stress the epoxy and can cause cracks in a bond line. It might be needed to subject the parts to a multiple temperature cycles. Quick changes in temperature would cause maximum stress.

  9. Combination of Heat and Pressure
  10. Epoxies are thermosetting resins which have a glass transition temperature (Tg). Heating above the Tg will soften the cured epoxy and allows de-bonding. When the adhesives become soft, it can be pried away more easily. Heating can be done with a soldering iron, hotplate or an oven..

  11. Boiling Water
  12. When epoxies are exposed to boiling for a longer period of time, the epoxies will lift away from most surfaces. Some mechanical action might be needed. This technique is suitable for embedding samples combined with thermal shock to crack the epoxy as long as the sample is compatible with the techniques used.

Note 1: When larger amounts of epoxy need to be removed, consider mechanical methods (cutting) before resorting to the techniques listed above.

Note 2: If epoxy used to bond a sample to a substrate for specimen preparation and the sample needs to be removed, consider using cyanoacrylate (superglue). Cyanoacrylate can be easily destroyed with a cyanoacrylate de-bonder.




SEM Supplies

TEM Supplies

Calibration

Sample Preparation

AFM / SPM

  Product Menu with Images
  SEM Sample Stubs
  Carbon Tabs
  Sample Stub Adapters
  SEM Stage Adapters
  SEM Sample Holders
  SEM Preparation Stands
  Filaments / Cathodes
  Silicon Finder Grid
  Gatan 3View Pins
  FEI Volumescope Pins
  SEM Stub Storage Boxes
  Phenom Supplies
  JEOL NeoScope Supplies
  Hitachi TM Series Supplies
  Field & Lab Sampler Kits
  FlowView liquid sample Kit

Instruments

  Acoustic Enclosures
  Cressington SEM coaters
  TEM Sample Prep
  Diaphragm Pump
  Rotary vacuum Pump
  Precision diamond saw  
  TEM Grids
  TEM Support Films
  Silicon Nitride Films
  K-Kit Wet Cell Holder
  Graphene Films
  TEM Grid Boxes
  Cryo Grid Boxes
  TEM Sample Staining
  3mm Embedding Tubes
  Filaments/Cathodes
  Eyelash Manipulators

Cryo Supplies

  Cryo Grid Boxes
  Other Cryo Supplies

FIB Supplies

  FIB Lift-out Grids
  FIB Low Profile Stubs
  FIB Grid Holders
  FIB Pre-tilt Holders
  FIB Pre-tilt stubs
  FIB Grid Boxes
  SEM / FIB Magn. Calib.
  SEM Res. Test Spec.
  EDS / WDS Calibration
  TEM Calibration
  AFM / SPM Calibration
  LM Magn. Calibration

Vacuum Supplies

  Vacuum Gauges
  KF/NW Vacuum Parts
  KF/NW Vacuum Hoses
  ISO Vacuum flange parts
  Vacuum Oil and Grease
  Vacuum Sealant
  Diaphragm Pump
  Rotary vacuum Pump
  Vacuum Sample Storage
  Vacuum Pick-Up Pens

Sample Coating Supplies

  Sputter Targets
  Carbon Rods & Fibers
  Quartz QCM Crystals
  SEM Sample Coating Fluid

Evaporation Supplies

  Thermal Evaporation Sources
  Evaporation Materials
  Supports & Substrates
  SEM Preparation Stands
  Tweezers
  Probes & Picks
  Applicators & Swabs
  Plastic Transfer Pipettes
  Cutting Tools / Scissors
  Conductive Paint/Cement
  Conductive Tapes & Tabs
  Non-Conductive Adhesives
  Sample Storage
  Hand Tools
  Sorting Wire Mesh
  Preparation Surfaces
  Cleaning / Gloves
  Conductive Metal Powders
  Metallographic Sample Prep
  AFM/SPM Discs
  AFM/SPM Disc Pick-up Tool
  AFM/SPM Holders
  AFM/SPM Disc Storage
  Cantilever Tweezers
  AFM/SPM Discs Tweezers
  Nano-Tec Mica Discs
  HOPG Substrates

Light Microscopy

  Correlative Cover Slips
  Glass Microscope Slides
  Glass Cover Slips
  Quartz Microscope Slides
  Quartz Cover Slips
  Black Metal Slides
  Slide Storage Boxes
  LM Calibration
  Plastic Transfer Pipettes
  Optical Lens Tissue
  Glass Petri Dishes
  Digital Microscope
  PTFE Beakers